Intrduction List of Grade Technical data(Grade) Technical data(Porperty) Topics       Catalogue download Press release Overseas branch Related links Contact Inquiry   TP82 Toyolac Parrel / Flame retardant V Properties Test Method Test Condition Units TP82 Tensile Strength ASTM-D638 23C/ 50%RH MPa kg/cm2 42 430 Tensile Elongation at Break 23C/ 50%RH % >10 Flexural Strength ASTM-D790 23C/ 50%RH MPa kg/cm2 65 660 Flexural Modulus 23C/ 50%RH MPa kg/cm2 2,060 21,000 Izod Impact Strength ASTM-D256 23C 12.7mm V-notched J/m kgcm/cm 118 12 -30C 12.7mm V-notched 39 4 23C 3.2mm V-notched 78 8 Distortion Temperature Under Load ASTM-D648 6.4mm 1.82MPa C 88 Rockwell Hardness ASTM-D785 23C/ 50%RH R-SCALE 105 Melt Flow Rate ISO-1133 220C/98N g/10min 28 Specific Gravity ASTM-D792 23C/ 50%RH - 1.14 Specific Surface Resistivity ASTM-D257 After injection molding 23C/50%RH 24hr 51011 Charged Voltage *TORAY V 1000 Charged Voltage Attenuation Half-Life *TORAY Sec. 0.8 Light Transmission JIS K7105 23C/ 50%RH 3mm % - Ball Pressure Temperature C 95 Flammability UL94 File No.E41797 1.50mmV-2 Mold Shrinkage % 0.5-0.8 Note ; These values are typical data for this product under specific test conditions and not intended for use as limiting specifications. *This grade doesn't contain specific bromine flame retardant {PBB, PBBE(O), PBDE(O), PBDPE(O)}.

Plastics Top