100G20
Fiberglass reinforced ABSG type / GF20% |
| Properties |
Test Method |
Test Condition |
Units |
100G20 |
| Tensile Strength |
ASTM-D638 |
23 C/
50%RH
|
MPa
kg/cm2
|
98
1,000
|
Tensile Elongation
at Break
|
23C/
50%RH
|
% |
3 |
| Flexural Strength |
ASTM-D790 |
23C/
50%RH
|
MPa
kg/cm2
|
140
1,430
|
| Flexural Modulus |
23C/
50%RH
|
MPa
kg/cm2
|
6,200
63,200
|
| Izod Impact Strength |
ASTM-D256 |
23C
12.7mm
V-notched
|
J/m
kg cm/cm
|
74
7.5
|
Distortion Temperature
Under Load
|
ASTM-D648 |
6.4mm
1.82MPa
|
C |
102 |
| Rockwell
Hardness |
ASTM-D785 |
23C/
50%RH
|
R-SCALE |
120 |
| Melt FlowRate |
ISO-1133 |
220C/98N |
g/10min |
11 |
| Specific Gravity |
ASTM-D792 |
23C/
50%RH
|
- |
1.18 |
| Ball Pressure
Temperature |
C |
95 |
| Flammability |
UL94
File No.E41797
|
HB equivalent |
| Mold Shrinkage |
% |
0.1-0.3 |
|
| Note ; These values are typical data for
this product under specific test conditions and not intended
for use as limiting specifications. |
|
|
|
|